Fused Alumina Magnesia Spinel
Talosaga


1.Ia lautele faʻaaogaina e uʻamea & uʻamea, sima ma pisinisi kilns alamanuia, ma isi
2.E masani ona faʻaaogaina e fausia ai vasega maualuga alumina-magnesia brick, maualuga le faʻatinoina alumina-magnesia castables, sliding nozzle, ladle brick, top brick for open hearth furnace etc.
3.It o se sili lelei mea e sui ai magnesia-chrome refractories. I se faʻaopopoga, o loʻo faʻaaogaina i oloa gaosi, o mea na muaʻi fausiaina, ma mea e le faʻafefeteina.
Grit ma Lelei efuefu
0.1-0 mm, 0.2-0 mm, 0.5-0 mm, 1-0 mm, 1-0.5 mm, 3-1 mm, 5-3 mm, 8-5 mm, 10-5 mm, 25-10 mm, 100 mata, 200 mesh, 325 mata ......
O isi spec e avanoa i luga ole talosaga.
Oloa Lelei
1.O le faʻaogaina o le eletise alualu i luma tilning ogaumu gaosiga faʻateleina le smelting vevela ma mafai ona faʻatumauina le tumau maualuga vevela gaosiga, ma faʻaleleia atili ai le tulaga lelei o le alumini-magnesium spinel.
2. E tusa ai ma manaʻoga eseese o tagata faʻatau mo le magnesium mea, e tele oloa talafeagai e gaosia. Feiloaʻi i tagata faʻatau manaʻoga manaʻoga.
3. Faʻaaogaina tekonolosi alualu i luma ma tekonolosi fua, o le le mama mea i totonu o le oloa e maualalo.
4. E mafai ona faʻaleleia mea e teteʻe atu i le faʻateʻia o le vevela ma mafai ona faʻaavanoaina ma le malosi e teteʻe ese ai.
5. E mafai ona faʻaleleia atili le toe faʻatauaina o toega otaota ma teteʻe atu i le vevela o le vevela ma le le mafai ona gaosia oloa.
Faagasologa faaliusuavai
Tilting Ogaumu - Fesuiaʻiga - Malulu Lalo - Barmac Crusher & Faʻavasegaina - Fausiaina oneone - Fale teu oloa
QC
I le magnesium aluminium spinel, o le vailaʻau o loʻo fai ma Al2O3, MgO, SiO2, Fe2O3, CaO susu, LOI manaʻomia le faʻataʻitaʻia, ma le anotusi o Al2O3 ma MgO manaʻomia le i luga 98%.
Vaega o vailaʻau
Vaega o vailaʻau |
MA-72 |
MA-75 |
MA-78 |
MA-85 |
Al2O3%≥ |
70 - 74 |
74 - 77 |
77 - 82 |
82 - 87 |
MgO%≤ |
24 - 28 |
21-24 |
16 - 21 |
11 - 16 |
SiO2%≤ |
0.4 |
0.4 |
0.4 |
0.4 |
Fe2O3%≤ |
0.25 |
0.25 |
0.25 |
0.25 |
Foliga manino %≤ |
5 |
3 |
3 |
3 |
Lautele Density g / cm3≥ |
3.3 |
3.3 |
3.3 |
3.3 |